BEHAVIOR OF Sm~(3+) IN SrFCl:Sm~(2+) IN THE PROCESS OF SPECTRAL HOLE-BURNING
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本文研究了77K时SrFCl:Sm~(2+)在光谱烧孔过程中Sm~(2+)和Sm~(3+)的再分布,得出烧孔的最大总面积受材料中Sm~(3+)数量的限制,孔的最大总面积与Sm~(2+)非均匀线型内积分面积比等于材料中Sm~(3+)与Sm~(2+)含量比。

    Abstract:

    The spectral hole-burning in SrFCl:Sm~(2+) at 77 K is studied. It has been obtained that the total area of holes in the inhomogeneous line shape is limited by the number of Sm~(3+) in the material and the maximum of total area (S_(hole)) of holes is proportional to the number of Sm~(3+). The integrated area (S_i) in the inhomogeneous line shape is proportional to the number of Sm~(2+) in the material. The value of'S_(hole)/S_i is equal to the ratio of the trivalent to the divalent samarium contents in the material.

    参考文献
    相似文献
    引证文献
引用本文

张家骅 黄世华. SrFCl:Sm^2+中的Sm^3+在光谱烧孔中的行为[J].红外与毫米波学报,1991,10(1):1~4]. ZHANG JIAHUA, HUANG SHIHUA, QIN WEIPING, GAO DIANKUN, YU JIAQI. BEHAVIOR OF Sm~(3+) IN SrFCl:Sm~(2+) IN THE PROCESS OF SPECTRAL HOLE-BURNING[J]. J. Infrared Millim. Waves,1991,10(1):1~4.]

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期:
  • 出版日期:
文章二维码