Microscopic luminescence and Raman scattering study was carried on AlInGaN quaternary alloy. Based on the analyses of SEM image and cathodoluminescence spectra measured around V-defects, the correlation between V-defect formation and indium segregation was clarified. Raman scattering of thin AlInGaN epilayers was investigated by using the short wavelength excitation of 325nm laser line. The frequency shift of A_1(LO) phonon induced by the change of Al composition in alloy was observed. The Raman scattering of LO phonons was found to be resonantly enhanced with outgoing resonance, and it is attributed to the cascade-like electron-multiphonon interaction mechanism.