The structural and optical properties of ZnxNi(1-x)Mn2O4 films grown on Pt/Ti/SiO2/Si substrate
Author:
Affiliation:

National Laboratory for Infrared Physics,Shanghai Institute of Technical Physics,Chinese Academy of Sciences;University of Chinese Academy of Sciences,National Laboratory for Infrared Physics,Shanghai Institute of Technical Physics,Chinese Academy of Sciences,School of Material Science and Engineering,University of Shanghai for Science and Technology,National Laboratory for Infrared Physics,Shanghai Institute of Technical Physics,Chinese Academy of Sciences,National Laboratory for Infrared Physics,Shanghai Institute of Technical Physics,Chinese Academy of Sciences,National Laboratory for Infrared Physics,Shanghai Institute of Technical Physics,Chinese Academy of Sciences,National Laboratory for Infrared Physics,Shanghai Institute of Technical Physics,Chinese Academy of Sciences

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用化学溶液法在Pt/Ti/SiO2/Si衬底上生长了ZnxNi1-xMn2O4(ZNMO, x=0, 0.05, 0.1, 0.15, 0.2, 0.25)尖晶石氧化物薄膜。X射线衍射(XRD)与场发射扫描电子显微镜(FESEM) 分析结果表明, Zn的掺杂浓度对ZNMO薄膜的结晶性和微结构有明显影响。用椭圆偏振光谱仪测量分析了ZNMO薄膜在300-1 100 nm波段的光学常数, 并讨论了Zn掺杂对折射率n和消光系数k的影响。在薄膜的拉曼光谱中观测到两个峰A1g与F2g, A1g模式的相对峰位随着Zn的掺杂浓度x的增大而减小。由于晶格应变与晶格失配, 拉曼峰峰位随Zn掺杂浓度的变化而轻微移动。

    Abstract:

    The spinel oxide ZnxNi1-xMn2O4 (ZNMO, x=0, 0.05, 0.1, 0.15, 0.2, 0.25) films have been grown on Pt/Ti/SiO2/Si substrate by chemical solution deposition (CSD) method. The crystallization and microstructural features of ZNMO films are studied by x-ray diffraction (XRD) and field-emission scanning electron microscopy (FESEM) analysis, respectively. The results show that the structural property of ZNMO films is affected by Zn concentration. The optical constants of ZNMO films have been analyzed by spectroscopic ellipsometry measurements in the wavelength range of 300-1 100 nm. The changes of the refractive index n and extinction coefficient k caused by Zn substituting are discussed. The A1g and F2g modes have been observed in Raman spectra. The relative intensity of the A1g mode decreases with increasing Zn concentration. The Raman peak positions shift slightly with Zn concentration x, which might result from lattice strain and lattice mismatch.

    参考文献
    相似文献
    引证文献
引用本文

王万胜,侯云,张增辉,周炜,高艳卿,吴敬,褚君浩.生长于Pt/Ti/SiO2/Si衬底的ZnxNi(1-x)Mn2O4薄膜的结构与光学性质[J].红外与毫米波学报,2016,35(6):676~680]. WANG Wan-Sheng, HOU Yun, ZHANG Zeng-Hui, ZHOU Wei, GAO Yan-Qing, WU Jing, CHU Jun-Hao. The structural and optical properties of ZnxNi(1-x)Mn2O4 films grown on Pt/Ti/SiO2/Si substrate[J]. J. Infrared Millim. Waves,2016,35(6):676~680.]

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2016-03-25
  • 最后修改日期:2016-09-27
  • 录用日期:2016-04-11
  • 在线发布日期: 2016-12-06
  • 出版日期: