长/长波双色二类超晶格红外探测器研究
作者:
作者单位:

1.华北光电技术研究所,北京 100015;2.中国科学院半导体研究所 半导体超晶格国家重点实验室,北京100083

作者简介:

通讯作者:

中图分类号:

TN214

基金项目:


Research on InAs/GaSb type-II superlattice dual-band long-/long-wavelength infrared photodetector
Author:
Affiliation:

1.North China Research Institute of Electro-optics, Beijing 100015, China;2.The State Key Laboratory of Superlattices and Microstructures, Institute of Semiconductors, Chinese Academy of Science, Beijing 100083, China

Fund Project:

Supported by the Equipment Model Development Project.

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    报道了长/长波双色二类超晶格红外焦平面探测器组件的研制。通过能带结构设计和分子束外延技术,获得了表面质量良好的长/长波双色超晶格外延材料。突破了长波超晶格低暗电流钝化、低损伤干法刻蚀等关键技术,制备出像元中心距30 μm的320×256长/长波双色InAs/GaSb超晶格焦平面探测器芯片。将芯片与双色读出电路互连,采用杜瓦封装,与制冷机耦合形成探测器组件。组件双波段50%后截止波长分别为7.7 μm(波段1)和10.0 μm(波段2)。波段1平均峰值探测率达到8.21×1010 cm·W-1·Hz1/2,NETD实现28.8 mK;波段2平均峰值探测率达到6.15×1010 cm·W-1·Hz1/2,NETD为37.8 mK,获得了清晰的成像效果,实现长/长波双色探测。

    Abstract:

    The development of type II superlattice dual-band long-/long-wavelength infrared focal plane photodetector is reported. Through the design of energy band structure and molecular beam epitaxial technology, dual-band long-/long-wavelength superlattice epitaxial material with good surface quality has been obtained. The 320×256 dual-band long-/long-wavelength InAs/GaSb superlattice focal plane photodetector with pixel center distance of 30 μm was prepared by breaking through the key technologies of low dark current passivation and low damage dry etching. The detector chip is interconnected with a dual color readout circuit, packaged in a Dewar package, and coupled to a refrigerator to form a detector assembly. The dual-band 50% cut-off wavelengths of the photodetector are 7.7 μm (band 1) and 10.0 μm (band 2), respectively. The average peak detectivity of band 1 reached 8.21×1010 cm·W-1·Hz1/2, and NETD achieved 28.8 mK. The average peak detectivity of band 2 reached 6.15×1010 cm·W-1·Hz1/2, and the NETD was 37.8 mK. Clear imaging of both colors has been achieved, demonstrating the realization of long-/long-wavelength dual-band photodetection.

    参考文献
    相似文献
    引证文献
引用本文

刘铭,游聪娅,李景峰,常发冉,温涛,李农,周朋,程雨,王国伟.长/长波双色二类超晶格红外探测器研究[J].红外与毫米波学报,2023,42(5):574~580]. LIU Ming, YOU Cong-Ya, LI Jing-Feng, CHANG Fa-Ran, WEN Tao, LI Nong, ZHOU Peng, CHENG Yu, WANG Guo-Wei. Research on InAs/GaSb type-II superlattice dual-band long-/long-wavelength infrared photodetector[J]. J. Infrared Millim. Waves,2023,42(5):574~580.]

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2023-03-22
  • 最后修改日期:2023-08-07
  • 录用日期:2023-06-06
  • 在线发布日期: 2023-08-04
  • 出版日期:
文章二维码