The infrared optical and mechanical properties of germanium carbide films prepared by ion beam sputtering
Author:
Affiliation:

Tianjin Jinhang Institute of Technical Physics,School of Electronic Information Engineering, Tianjin University

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用离子束溅射法通过在CH4和Ar 的混合气体中溅射Ge靶材制备碳化锗(Ge1-xCx)薄膜.分别通过原子力显微镜、拉曼光谱和X射线光电子能谱、傅里叶变换红外光谱以及纳米压痕测试研究了薄膜的表面形貌、化学结构、光学特性和力学特性.同时分析了制备薄膜时的离子源束压和薄膜性质之间的关系.结果表明,薄膜的粗糙度随束压的增大而减小.在较高束压下制备的薄膜含有较少的C元素和较多的Ge-C键.薄膜具有非常好的红外光学特性和力学特性.薄膜在较大波长范围内具有良好的透光性能.C元素含量随着束压的升高而降低,进而导致薄膜的折射率在束压从300 V增大到800 V的过程中逐渐升高.薄膜的硬度大于8 GPa.由于薄膜中的Ge-C键代替了C-C 键和C-Hn键,薄膜的硬度随束压的增加逐渐增加.

    Abstract:

    Germanium carbon (Ge1-xCx) thin films were deposited by ion beam sputtering deposition of Ge target in a CH4/Ar discharge. The surface morphology, chemical structure, infrared optical and mechanical properties of the Ge1-xCx films were investigated by atomic force microscopy (AFM), Raman spectroscopy, X-ray photoelectron spectroscopy(XPS), Fourier transform infrared (FTIR) spectroscopy and nano-indentation, respectively. The relationship between ion beam voltage and film properties was discussed. The results show that the surface roughness decreases with increasing of the ion beam voltage. The film deposited at a higher voltage has lower carbon content and higher fraction of Ge-C bonds. The film has excellent infrared optical and mechanical properties. The films show good transparent over a wide range. Due to the content of the carbon decreasing with increasing of voltage, the refractive index increases obviously as the ion beam voltage increases from 300 V to 800 V. The hardness of the film is above 8 GPa. With the Ge-C bonds instead of the C-C bonds and C-Hn bonds, the hardness of the film increases with increasing ion beam voltage

    参考文献
    相似文献
    引证文献
引用本文

孙鹏,胡明,张锋,季一勤,刘华松,刘丹丹,冷健,杨明,李珏.(英)离子束溅射法制备碳化锗薄膜的红外光学特性和力学特性[J].红外与毫米波学报,2016,35(2):133~138]. SUN Peng, HU Mng, ZHANG Feng, JI Yi-Qin, LIU Hua-Song, LIU Dan-Dan, LENG Jian, YANG Ming, LI Jue. The infrared optical and mechanical properties of germanium carbide films prepared by ion beam sputtering[J]. J. Infrared Millim. Waves,2016,35(2):133~138.]

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2015-06-18
  • 最后修改日期:2015-12-23
  • 录用日期:2015-08-04
  • 在线发布日期: 2016-05-11
  • 出版日期:
文章二维码